Acetic Glass Silicone Sealant OLV3010

1,one part,acetic cure 2,one of very popular product, very competitive price 3,general purpose glazing with good weatherproof

Description:

OLV3010 Acetic Silicone Glass Sealant is one-part room temperature acetoxy silicone sealant. It is widely used, durable general filler for glasses, windows and doors, good adhesion to other common construction materials.

Main purposes:

1,  For sealing glasses, windows and doors;

2,  For sealing aluminum alloy, ceramic, glass fiber, non-oily wood

Characteristics:

1,  One-component, acetic cured.

2,  Easy to use, cured quickly, good weatherability ;

3,  Good adhesion to many building materials;

4,  Colors include clear, white, grey and black, or other colors as per customers’ requirements.

Application:

1.  Clean with solvents such as toluene or acetone to keep the substrate surfaces completely clean and dry;

2.  Fully filling the gap for better sealing to the surfaces of the material.

3.  For better appearance cover outside of joint areas with masking taps before application;

4.  Cut nozzle to desired size and extrudes sealant to joint areas;

5.  Tool immediately after sealant application and remove masking tape before sealant skins.

Limitations:

1.  Certain corrosion to cement, marble, coated glass, copper, lead, zinc-coated materials.

2.  Unsuitable for curtain wall structural adhesive; 

3.  Unsuitable for the airproof location, because it is required to absorb moisture in air to cure for the sealant; 

4.  Unsuitable for the frosty or moist surface; 

5.  Unsuitable for the continually soggy place;

6.  Can’t be used if the temperature is below 4°C or above 50°C on the surface of the material.

Shelf life: 12 months if keep sealing, and stored below 270C in cool, dry place after the date of production.

Technology data:

The following data are only for reference purpose, not intended for use in preparing specification.

OLV3010 Acetic Silicone Glass Sealant
Model No	3010	Testing Method
Test at 50±5% RH and temperature 23±20C:
Density(g/cm3)	0.956	GB/T 13477
Drying Time(min)	8	GB/T 13477
Extrusion(ml/min)	1249	GB/T 13477
Curing Speed(mm/d)	3	GB/T 13477
As Cured -After 21 days at 50±5% RH and temperature 23±20C:
Hardness(shore A)	25	GB/T 531
Tensile Strength(Mpa)	0.28	GB/T 13477
Elongation of Rupture(%)	120.3	GB/T 13477
Movement Capacity	12.5	GB/T 13477
Storage	12 months

Acetic Glass Silicone Sealant OLV3010